A283 Grade C steel: the preferred material for medium and low strength applications

A283 Grade C concept: A283 Grade C is a steel grade under the American Society for Testing and Materials (ASTM) standard. It is a carbon structural steel, mainly composed of iron, carbon and a small amount of manganese, silicon and other elements. Through strict composition control and production process, the consistency and stability of steel performance are guaranteed.

A283 Grade C features: moderate strength, yield strength of about 170-205MPa, tensile strength of 345-450MPa, can meet the load-bearing requirements of general structural parts; has good ductility and plasticity, easy to cold and hot processing; at the same time, excellent welding performance, can be connected with other steels through common welding processes, but the corrosion resistance is general, and anti-rust measures need to be taken.

A283 Grade C Size: A283 Grade C steel plate thickness specifications vary, generally 6 - 100mm, width and length can be customized according to demand, common width 1000 - 3000mm, length 2000 - 12000mm; round steel diameter range is usually 10 - 200mm, which can meet the size requirements of different engineering structures.

A283 Grade C Application Scope: Commonly used in building structures with low strength requirements, such as non-main load-bearing components of residential buildings and small commercial buildings; in the field of machinery manufacturing, it is used to manufacture some parts with less stress, such as brackets, bases, etc.; it is also suitable for temporary structures and agricultural facilities that are more sensitive to cost, effectively controlling costs while ensuring structural safety.