The following methods can be used to reduce the welding stress and deformation of ASTM CortenA weathering steel:
(1) Reverse deformation method; (2) Reasonable installation and welding sequence; (3) Rigid fixing method; (4) Heat dissipation method; (5) H
When the Q355NH weathering steel plate with a thickness of more than 10 mm is rolled in the rolling pit, after the wear-resistant liner bites into the rolling mill, the splint should be opened quickly to reduce the gap between the Q355NH weathering steel
Q355NH weathering steel is composed of the following alloy components by weight: carbon: 0.12-0.21, silicon: 0.2-2.0, manganese: 0.7-2.0, sulfur ≤0.036, phosphorus ≤0.034, copper: 0.10-0.40, aluminum:0.2, the remaining is iron and trace impurities.
We can supply the Q355NH weathering steel plate with high quality and low price. If you want to know more about Q355NH weathering steel plate, please contact us freely. Our sale person will contact you as soon as possible.
Q355NH weathering steel plate is characterized by uniform rust red color, good color fastness and adhesion, no peeling, no slag falling, no rust water flowing in the later stage, and super corrosion resistance.
After welding, cooling and shrinkage can be uniform at the same time, so as to significantly reduce the ASTM A588 Grade C weathering steel plate welding stress and welding deformation. Post-welding heat treatment of ASTM A588 Grade C weathering steel plat
Full annealing. The process of heating Q295NH steel plate to 30~50℃ above AC3, complete austenitizing, followed by slow cooling, and obtaining near equilibrium microstructure is called complete annealing. Mainly used for medium carbon carbon steel and med
The purpose of Q295NH weathering steel plate annealing is as follows: reduce the hardness of Q295NH weathering steel plate, improve the plasticity, in order to facilitate cutting and cold deformation processing.
Reduce or eliminate the internal stress of JIS G3114 SMA 50 AW steel plate during quenching to prevent deformation and cracking of workpiece. The toughness of JIS G3114 SMA 50 AW steel plate was improved by tempering, and the strength and hardness of JIS
The purpose of quenching is to improve the hardness, strength and wear resistance of EN10025-5 S235J2W steel plate, and give full play to the performance potential of EN10025-5 S235J2W steel plate. However, quenched martensite is not the final structure r