Corten B steel Surface Protection and Treatment Technology

Corten B steel Surface Protection and Treatment Technology

In order to ensure that the overall weather resistance of Corten B steel is consistent and avoid the decline in local corrosion resistance, a complete set of surface protection technology for Corten B steel has been formulated, that is, it is strictly for

Welding performance of UNI Fe 510 D2K1 weathering steel

Welding performance of UNI Fe 510 D2K1 weathering steel

Because weathering elements such as Cr, Ni, and Cu are added to UNI Fe 510 D2K1 weathering steel, the carbon equivalent is high, and the weldability of UNI Fe 510 D2K1 weathering steel is worse than ordinary bridge steel, and welding cracks, pores, slag i

ASTM A588 Gr.A Steel for Bridge Manufacturing

ASTM A588 Gr.A Steel for Bridge Manufacturing

In recent years, China is actively promoting the construction of ASTM A588 Gr.A steel bridges. ASTM A588 Gr.A steel is used to manufacture bridges, which can be used without painting. While meeting the requirements of energy saving and environmental prote

Study on surface anticorrosion of Q355GNH weathering steel

Study on surface anticorrosion of Q355GNH weathering steel

Some coastal bridge supports need to be made of Q355GNH weathering steel plate, and the anti-corrosion requirements must meet the relevant railway standards such as TB/T 1527-2011 and GB/T 9779-2011. In this study, several surface treatment processes of Q

S355JR and Q345B, Q355GNH weather performance comparison

S355JR and Q345B, Q355GNH weather performance comparison

Ordinary carbon steel Q345B and S355JR and weathering steel Q255GNH were placed in a non-specially humid environment indoors to investigate their weathering performance. When Q345B and S355JR were placed for 1 week, rust began to appear on the surface; wh

Measures to change the deformation of SPHC weathering steel plate

Measures to change the deformation of SPHC weathering steel plate

By studying the uniformity of deformation between racks and the uniformity of laminar cooling, it is analyzed that the main reason for the poor shape of SPHC weathering steel plates is the uneven cooling of laminar flow.

S355J2W steel welded joints have good mechanical properties

The microstructure of the weld zone of S355J2W steel welded joints air-cooled is composed of coarse columnar ferrite, network ferrite, acicular ferrite and a small amount of pearlite, and the microstructure of the heat-affected zone is composed of fine an

12mm thick S355J2W weathering steel welding process and impact test

The test material is 12mm thick S355J2W weathering steel, using MAG welding (melting electrode active gas shielded arc welding) multi-layer multi-pass welding process, the shielding gas is 80% Ar+ 20% CO2 mixed gas, the joint form is butt joint, V-shaped

Effect of Grain Size on Corten B Weathering Steel

For the Corten B weathering steel experiment, under the same corrosion environment and the potential difference between grain boundaries and grains, compared with samples with larger grain sizes, the k value of the sample with smaller grain size Smaller,

BBN Research on S355J2WP weathering steel Surface Rust Layer Technology

The requirements for environmental protection of steel structure buildings are increasing at home and abroad, and the surface treatment technology of S355J2WP weathering steel should also be developed towards environmental friendliness. Therefore, BBN pro

 856   Home Pre 25 26 27 28 29 30 31 32 33 34 Next End

Technology

Contact Us

  • Address: Xichen Science & Technology Building High-tech Development Zone, Zhengzhou, China
  • Tel: 0086-371-86151827
  • Fax: 0086-371-86011881
  • Email: [email protected]
Looking for Corten A steel, Weathering steel plates? BBN Group is a good choice.